Liquid crystal medium and high-frequency components containing the same

ABSTRACT

The present invention relates to liquid-crystalline media comprising
         at least one compound of the formula I and   at least one compound of the formula II
 
or
   at least one compound of the formula I and   at least one compound of the formula III
 
or
   at least one compound of the formula II and   at least one compound of the formula III
 
or
   at least one compound of the formula I and   at least one compound of the formula II and   at least one compound of the formula III:       

     
       
         
         
             
             
         
       
     
     in which the parameters have the meaning indicated in Claim  1 , and to components comprising these media for high-frequency technology, in particular phase shifters and microwave array antennas.

FIELD OF THE INVENTION

The present invention relates to liquid-crystalline media and to high-frequency components comprising same, especially microwave components for high-frequency devices, such as devices for shifting the phase of microwaves, in particular for microwave phased-array antennas.

PRIOR ART AND PROBLEM TO BE SOLVED

Liquid-crystalline media have a been used for some time in electro-optical displays (liquid crystal displays—LCDs) in order to display information.

U.S. Pat. No. 7,183,447 discloses various laterally fluorinated, mesogenic quaterphenyl compounds.

U.S. Pat. No. 7,211,302 discloses, inter alia, liquid-crystalline media which, besides polar terphenyl compounds of the formulae

also comprise small amounts of quaterphenyl compounds of the formula

in order to improve the stability of the media, in particular to UV irradiation.

Recently, however, liquid-crystalline media have also been proposed for use in components for microwave technology, such as, for example, in DE 10 2004 029 429 A and in JP 2005-120208 (A).

As a typical microwave application, the concept of the inverted microstrip line as described by K. C. Gupta, R. Garg, I. Bahl and P. Bhartia: Microstrip Lines and Slotlines, 2^(nd) ed., Artech House, Boston, 1996, is employed, for example, in D. Dolfi, M. Labeyrie, P. Joffre and J. P. Huignard: Liquid Crystal Microwave Phase Shifter. Electronics Letters, Vol. 29, No. 10, pp. 926-928, May 1993, N. Martin, N. Tentillier, P. Laurent, B. Splingart, F. Huert, P H. Gelin, C. Legrand: Electrically Microwave Tunable Components Using Liquid Crystals. 32^(nd) European Microwave Conference, pp. 393-396, Milan 2002, or in Weil, C.: Passiv steuerbare Mikrowellenphasenschieber auf der Basis nichtlinearer Dielektrika [Passively Controllable Microwave Phase Shifters based on Nonlinear Dielectrics], Darmstädter Dissertationen D17, 2002, C. Weil, G. Lüssem, and R. Jakoby: Tunable Invert-Microstrip Phase Shifter Device Using Nematic Liquid Crystals, IEEE MTT-S Int. Microw. Symp., Seattle, Wash., June 2002, pp. 367-370, together with the commercial liquid crystal K15 from Merck KGaA. C. Weil, G. Lüssem, and R. Jakoby: Tunable Invert-Microstrip Phase Shifter Device Using Nematic Liquid Crystals, IEEE MTT-S Int. Microw. Symp., Seattle, Wash., June 2002, pp. 367-370, achieve phase shifter qualities of 12°/dB at 10 GHz with a control voltage of about 40 V therewith. The insertion losses of the LC, i.e. the losses caused only by the polarisation losses in the liquid crystal, are given as approximately 1 to 2 dB at 10 GHz in Weil, C.: Passiv steuerbare Mikrowellenphasenschieber auf der Basis nichtlinearer Dielektrika [Passively Controllable Microwave Phase Shifters based on Nonlinear Dielectrics], Darmstädter Dissertationen D17, 2002. In addition, it has been determined that the phase shifter losses are determined primarily by the dielectric LC losses and the losses at the waveguide junctions. T. Kuki, H. Fujikake, H. Kamoda and T. Nomoto: Microwave Variable Delay Line Using a Membrane Impregnated with Liquid Crystal. IEEE MTT-S Int. Microwave Symp. Dig. 2002, pp. 363-366, June 2002, and T. Kuki, H. Fujikake, T. Nomoto: Microwave Variable Delay Line Using Dual-Frequency Switching-Mode Liquid Crystal. IEEE Trans. Micro-wave Theory Tech., Vol. 50, No. 11, pp. 2604-2609, November 2002, also address the use of polymerised LC films and dual-frequency switching-mode liquid crystals in combination with planar phase shifter arrangements.

A. Penirschke, S. Müller, P. Scheele, C. Weil, M. Wittek, C. Hock and R. Jakoby: “Cavity Perturbation Method for Characterization of Liquid Crystals up to 35 GHz”, 34^(th) European Microwave Conference—Amsterdam, pp. 545-548 describe, inter alia, the properties of the known single liquid-crystalline substance K15 (Merck KGaA, Germany) at a frequency of 9 GHz.

A. Gaebler, F. Goelden, S. Müller, A. Penirschke and R. Jakoby “Direct Simulation of Material Permittivites using an Eigen-Susceptibility Formulation of the Vector Variational Approach”, 12MTC 2009—International Instrumentation and Measurement Technology Conference, Singapore, 2009 (IEEE), pp. 463-467, describe the corresponding properties of the known liquid-crystal mixture E7 (likewise Merck KGaA, Germany).

DE 10 2004 029 429 A describes the use of liquid-crystal media in microwave technology, inter alia in phase shifters. DE 10 2004 029 429 A has already investigated liquid-crystalline media with respect to their properties in the corresponding frequency range. In addition, it describes liquid-crystalline media which comprise compounds of the formulae

besides compounds of the formulae

or besides compounds of the formulae

However, these compositions are afflicted with serious disadvantages. Most of them result, besides other deficiencies, in disadvantageously high losses and/or inadequate phase shifts or inadequate material quality.

For these applications, liquid-crystalline media having particular, hitherto rather unusual, uncommon properties, or combinations of properties, are required.

Novel liquid-crystalline media having improved properties are thus necessary. In particular, the loss in the microwave region must be reduced and the material quality (η) must be improved.

In addition, there is a demand for an improvement in the low-temperature behaviour of the components. Both an improvement in the operating properties and also in the shelf life are necessary here.

There is therefore a considerable demand for liquid-crystalline media having suitable properties for corresponding practical applications.

PRESENT INVENTION

Surprisingly, it has now been found that it is possible to achieve liquid-crystalline media having a suitably high Δ∈, a suitable, nematic phase range and Δn which do not have the disadvantages of the prior-art materials, or at least only do so to a considerably reduced extent.

These improved liquid-crystalline media in accordance with the present invention comprise

-   -   at least one compound of the formula I and     -   at least one compound of the formula II         or     -   at least one compound of the formula I and     -   at least one compound of the formula III         or     -   at least one compound of the formula II and     -   at least one compound of the formula III         or     -   at least one compound of the formula I and     -   at least one compound of the formula II and     -   at least one compound of the formula III

in which

-   L¹¹ denotes R¹¹ or X¹¹, -   L¹² denotes R¹² or X¹², -   R¹¹ and R¹², independently of one another, denote H, unfluorinated     alkyl or unfluorinated alkoxy having 1 to 17, preferably having 3 to     10, C atoms or unfluorinated alkenyl, unfluorinated alkenyloxy or     unfluorinated alkoxyalkyl having 2 to 15, preferably 3 to 10, C     atoms, preferably alkyl or unfluorinated alkenyl, -   X¹¹ and X¹², independently of one another, denote H, F, Cl, —CN,     —NCS, —SF₅, fluorinated alkyl or fluorinated alkoxy having 1 to 7 C     atoms or fluorinated alkenyl, unfluorinated or fluorinated     alkenyloxy or unfluorinated or fluorinated alkoxyalkyl having 2 to 7     C atoms, preferably fluorinated alkoxy, fluorinated alkenyloxy, F or     Cl, and

-   -   independently of one another, denote

in which

-   L²¹ denotes R²¹ and, in the case where Z²¹ and/or Z²² denote     trans-CH═CH— or trans-CF═CF—, alternatively denotes X²¹, -   L²² denotes R²² and, in the case where Z²¹ and/or Z²² denote     trans-CH═CH— or trans-CF═CF—, alternatively denotes X²², -   R²¹ and R²², independently of one another, denote H, unfluorinated     alkyl or unfluorinated alkoxy having 1 to 17, preferably having 3 to     10, C atoms or unfluorinated alkenyl, unfluorinated alkenyloxy or     unfluorinated alkoxyalkyl having 2 to 15, preferably 3 to 10, C     atoms, preferably alkyl or unfluorinated alkenyl, -   X²¹ and X²², independently of one another, denote F or Cl, —CN,     —NCS, —SF₅, fluorinated alkyl or alkoxy having 1 to 7 C atoms or     fluorinated alkenyl, alkenyloxy or alkoxyalkyl having 2 to 7 C     atoms, or —NCS, preferably —NCS,     one of -   Z²¹ and Z²² denotes trans-CH═CH—, trans-CF═CF— or —C≡C— and the     other, independently thereof, denotes trans-CH═CH—, trans-CF═CF— or     a single bond, preferably one of them denotes —C≡C— or trans-CH═CH—     and the other denotes a single bond, and

-   -   independently of one another, denote

in which

-   L³¹ denotes R³¹ or X³¹, -   L³² denotes R³² or X³², -   R³¹ and R³², independently of one another, denote H, unfluorinated     alkyl or unfluorinated alkoxy having 1 to 17, preferably having 3 to     10, C atoms or unfluorinated alkenyl, unfluorinated alkenyloxy or     unfluorinated alkoxyalkyl having 2 to 15, preferably 3 to 10, C     atoms, preferably alkyl or unfluorinated alkenyl, -   X³¹ and X³², independently of one another, denote H, F, Cl, —CN,     —NCS, —SF₅, fluorinated alkyl or fluorinated alkoxy having 1 to 7 C     atoms or fluorinated alkenyl, unfluorinated or fluorinated     alkenyloxy or unfluorinated or fluorinated alkoxyalkyl having 2 to 7     C atoms, preferably fluorinated alkoxy, fluorinated alkenyloxy, F or     Cl, and -   Z³¹ to Z³³, independently of one another, denote trans-CH═CH—,     trans-CF═CF—, —C≡C— or a single bond, preferably one or more of them     denotes a single bond, particularly preferably all denote a single     bond, and

-   -   independently of one another, denote

In a preferred embodiment of the present invention, the liquid-crystalline media comprise one or more compounds of the formula I and one or more compounds of the formula III.

In a further preferred embodiment of the present invention, the liquid-crystalline media comprise one or more compounds of the formula I and one or more compounds of the formula II.

The liquid-crystalline media in accordance with the present invention likewise preferably comprise one or more compounds of the formula II and one or more compounds of the formula III.

Particular preference is given in accordance with the present invention to liquid-crystalline media which comprise one or more compounds of the formula I, one or more compounds of the formula II and one or more compounds of the formula III.

The liquid-crystalline media in accordance with the present application preferably comprise in total 15 to 90%, preferably 20 to 85% and particularly preferably 25 to 80%, of compounds of the formula I. The liquid-crystalline media in accordance with the present application preferably comprise in total 1 to 70%, preferably 2 to 65% and particularly preferably 3 to 60%, of compounds of the formula II.

The liquid-crystalline media in accordance with the present application preferably comprise in total 0 to 60%, preferably 5 to 55% and particularly preferably 10 to 50%, of compounds of the formula III.

In a preferred embodiment of the present invention, in which the liquid-crystalline media comprise in each case one or more compounds of the formulae I, II and III, the concentration of the compounds of the formula I is preferably 45 to 75%, preferably 50 to 70% and particularly preferably 55 to 65%, the concentration of the compounds of the formula II is preferably 1 to 20%, preferably 2 to 15% and particularly preferably 3 to 10%, and the concentration of the compounds of the formula III is preferably 1 to 30%, preferably 5 to 25% and particularly preferably 5 to 20%.

In a further preferred embodiment of the present invention, in which the liquid-crystalline media comprise in each case one or more compounds of the formulae I, II and III, the concentration of the compounds of the formula I is preferably 15 to 40%, preferably 20 to 35% and particularly preferably 25 to 30%, the concentration of the compounds of the formula II is preferably 10 to 35%, preferably 15 to 30% and particularly preferably 20 to 25%, and the concentration of the compounds of the formula III is preferably 25 to 50%, preferably 30 to 45% and particularly preferably 35 to 40%.

In a preferred embodiment of the present invention, in which the liquid-crystalline media comprise in each case one or more compounds of the formulae I and II, but at most 5% and preferably no compounds of the formula III, the concentration of the compounds of the formula I is preferably 10 to 50%, preferably 20 to 40% and particularly preferably 25 to 35%, the concentration of the compounds of the formula II is preferably 40 to 70%, preferably 50 to 65% and particularly preferably 55 to 60%, and the concentration of the compounds of the formula III is preferably 1 to 4%, preferably 1 to 3% and particularly preferably 0%.

The liquid-crystalline media in accordance with the present application particularly preferably comprise in total 50 to 80%, preferably 55 to 75% and particularly preferably 57 to 70%, of compounds of the formula I-1 and/or in total 5 to 70%, preferably 6 to 50% and particularly preferably 8 to 20% of compounds selected from the group of the compounds of the formulae I-2 and I-3.

The liquid-crystalline media in accordance with the present application likewise preferably comprise in total 5 to 60%, preferably 10 to 50% and particularly preferably 7 to 20% of compounds of the formula II.

In the case of the use of a single homologous compound, these limits correspond to the concentration of this homologue, which is preferably 2 to 20%, particularly preferably 1 to 15%. In the case of the use of two or more homologues, the concentration of the individual homologues is likewise preferably in each case 1 to 15%.

The compounds of the formulae I to III in each case include dielectrically positive compounds having a dielectric anisotropy of greater than 3, dielectrically neutral compounds having a dielectric anisotropy of less than 3 and greater than −1.5 and dielectrically negative compounds having a dielectric anisotropy of −1.5 or less.

In a preferred embodiment of the present invention, the liquid-crystal medium comprises one or more compounds of the formula I, preferably selected from the group of the compounds of the formulae I-1 to I-3, preferably of the formulae I-1 and/or I-2 and/or I-3, preferably of the formulae I-1 and I-2, more preferably these compounds of the formula I predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which the parameters have the respective meanings indicated above for formula I and preferably

-   R¹¹ denotes unfluorinated alkyl having 1 to 7 C atoms or     unfluorinated alkenyl having 2 to 7 C atoms, -   R¹² denotes unfluorinated alkyl having 1 to 7 C atoms or     unfluorinated alkenyl having 2 to 7 C atoms or unfluorinated alkoxy     having 1 to 7 C atoms, -   X¹¹ and X¹², independently of one another, denote F, Cl, —OCF₃,     —CF₃, —CN, —NCS or —SF₅, preferably F, Cl, —OCF₃ or —CN.

The compounds of the formula I-1 are preferably selected from the group of the compounds of the formulae I-1a to I-1d, more preferably these compounds of the formula I-1 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which the parameters have the respective meanings indicated above for formula I-1 and in which

-   Y¹¹ and Y¹² each, independently of one another, denote H or F, and     preferably -   R¹¹ denotes alkyl or alkenyl, and -   X¹¹ denotes F, Cl or —OCF₃.

The compounds of the formula I-2 are preferably selected from the group of the compounds of the formulae I-2a to I-2e and/or from the group of the compounds of the formulae I-2f and I-2g, more preferably these compounds of the formula I-2 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

where in each case the compounds of the formula I-2a are excluded from the compounds of the formulae I-2b and I-2c, the compounds of the formula I-2b are excluded from the compounds of the formulae I-2c and the compounds of the formula I-2g are excluded from the compounds of the formulae I-2f, and in which the parameters have the respective meanings indicated above for formula I-1 and in which

-   Y¹¹ and Y¹² each, independently of one another, denote H or F, and     preferably -   R¹¹ denotes alkyl or alkenyl, -   X¹¹ denotes F, Cl or —OCF₃, and preferably one of -   Y¹¹ and Y¹² denotes H and the other denotes H or F, preferably     likewise denotes H.

The compounds of the formula I-3 are preferably compounds of the formula I-3a:

in which the parameters have the respective meanings indicated above for formula I-1 and in which preferably

-   X¹¹ denotes F, Cl, preferably F, -   X¹² denotes F, Cl or —OCF₃, preferably —OCF₃.

In an even more preferred embodiment of the present invention, the compounds of the formula I are selected from the group of the compounds I-1a to I-1d, preferably selected from the group of the compounds I-1c and I-1d, more preferably the compounds of the formula I predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

The compounds of the formula I-1a are preferably selected from the group of the compounds I-1a-1 and I-1a-2, more preferably these compounds of the formula I-1a predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which

-   R¹¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1), in which -   n denotes an integer in the range from 0 to 7, preferably in the     range from 1 to 5 and particularly preferably 3 or 7.

The compounds of the formula I-1b are preferably compounds of the formula I-1b-1:

in which

-   R¹¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1), in which -   n denotes an integer in the range from 0 to 15, preferably in the     range from 1 to 7 and particularly preferably 1 to 5.

The compounds of the formula I-1c are preferably selected from the group of the compounds of the formulae I-1c-1 and I-1c-4, preferably selected from the group of the compounds of the formulae I-1c-1 and I-1c-2, more preferably these compounds of the formula I-1c predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which

-   R¹¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1), in which -   n denotes an integer in the range from 0 to 15, preferably in the     range from 1 to 7 and particularly preferably 1 to 5.

The compounds of the formula I-1d are preferably selected from the group of the compounds of the formulae I-1d-1 and I-1d-2, preferably the compound of the formula I-1d-2, more preferably these compounds of the formula I-1d predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which

-   R¹¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1), in which -   n denotes an integer in the range from 0 to 15, preferably in the     range from 1 to 7 and particularly preferably 1 to 5.

The compounds of the formula I-2a are preferably selected from the group of the compounds of the formulae I-2a-1 and I-2a-2, preferably the compounds of the formula I-1a-1, more preferably these compounds of the formula I-2a predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which

-   R¹¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R¹² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

Preferred combinations of (R¹¹ and R¹²), in particular in formula I-2a-1, are (C_(n)H_(2n+1) and C_(m)H_(2m+1)), (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)), (CH₂═CH—(CH₂)_(Z) and C_(m)H_(2m+1)), (CH₂═CH—(CH₂)_(Z) and O—C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and (CH₂)_(Z)—CH═CH₂).

Preferred compounds of the formula I-2b are the compounds of the formula I-2b-1:

in which

-   R¹¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R¹² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combination of (R¹¹ and R¹²) here is, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

Preferred compounds of the formula I-2c are the compounds of the formula I-2c-1:

in which

-   R¹¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R¹² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combination of (R¹¹ and R¹²) here is, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

Preferred compounds of the formula I-2d are the compounds of the formula I-2d-1:

in which

-   R¹¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R¹² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combination of (R¹¹ and R¹²) here is, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

Preferred compounds of the formula I-2e are the compounds of the formula I-2e-1:

in which

-   R¹¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R¹² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combination of (R¹¹ and R¹²) here is, in particular, (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)).

Preferred compounds of the formula I-2f are the compounds of the formula I-2f-1.

in which

-   R¹¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R¹² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R¹¹ and R¹²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)), particularly preferably (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

Preferred compounds of the formula I-2g are the compounds of the formula I-2g-1:

in which

-   R¹¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R¹² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R¹¹ and R¹²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)), particularly preferably (C_(n)H_(2n+1) and O—C_(m) H _(2m+1)).

The compounds of the formula II are preferably selected from the group of the compounds of the formulae II-1 to II-4, more preferably these compounds of the formula II predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which

-   Z²¹ and Z²² denote trans-CH═CH— or trans-CF═CF—, preferably     trans-CH═CH—, and the other parameters have the meaning given above     under formula II, and preferably -   R²¹ and R²², independently of one another, denote H, unfluorinated     alkyl or alkoxy having 1 to 7 C atoms or unfluorinated alkenyl     having 2 to 7 C atoms, -   X²² denotes F, Cl, —CN or —NCS, preferably —NCS,     and one of

-   -   and the others, independently of one another, denote

-   R²¹ denotes C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R²² denotes C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂,     and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2,     and where the compounds of the formula II-2 are excluded from the     compounds of the formula II-1.

The compounds of the formula II-1 are preferably selected from the group of the compounds of the formulae II-1a and II-1b, preferably selected from the group of the compounds of the formula II-1a, more preferably these compounds of the formula II-1 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which

-   R²¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R²² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R²¹ and R²²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)), particularly preferably (C_(n)H_(2n+1) and C_(m)H_(2m+1)) in the case of formula II-1a and particularly preferably (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)) in the case of formula II-1b.

The compounds of the formula II-2 are preferably compounds of the formula II-2a:

in which

-   R²¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R²² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R²¹ and R²²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)).

The compounds of the formula II-3 are preferably compounds of the formula II-3a:

in which the parameters have the meanings indicated above for formula II-3 and preferably

-   R²¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1)) in which -   n denotes an integer in the range from 0 to 7, preferably in the     range from 1 to 5, and -   X²² denotes —F, —Cl, —OCF₃, —CN or —NCS, particularly preferably     —NCS.

The compounds of the formula II-4 are preferably compounds of the formula II-4a:

in which the parameters have the meanings indicated above for formula II-4 and preferably

-   R²¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1), in which -   n denotes an integer in the range from 0 to 7, preferably in the     range from 1 to 5, and -   X²² denotes —F, —Cl, —OCF₃, —CN or —NCS, particularly preferably     —NCS.

Further preferred compounds of the formula II are the compounds of the following formulae:

in which

-   n denotes an integer in the range from 0 to 7, preferably in the     range from 1 to 5.

The compounds of the formula III are preferably selected from the group of the compounds of the formulae III-1 to III-7, more preferably these compounds of the formula III predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

where the compounds of the formula III-5 are excluded from the compounds of the formula III-6, and in which the parameters have the respective meanings indicated above for formula I and preferably

-   R³¹ denotes unfluorinated alkyl or alkoxy, each having 1 to 7 C     atoms, or unfluorinated alkenyl having 2 to 7 C atoms, -   R³² denotes unfluorinated alkyl or alkoxy, each having 1 to 7 C     atoms, or unfluorinated alkenyl having 2 to 7 C atoms, and -   X³² denotes F, Cl, or —OCF₃, preferably F, and particularly     preferably -   R³¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R³² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The compounds of the formula III-1 are preferably selected from the group of the compounds of the formulae III-1a to III-1d, more preferably these compounds of the formula III-1 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which X³² has the meaning given above for formula III-2 and

-   R³¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1), in which -   n denotes 1 to 7, preferably 2 to 6, particularly preferably 2, 3 or     5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2, and -   X³² preferably denotes F.

The compounds of the formula III-2 are preferably selected from the group of the compounds of the formulae III-2a and III-2b, preferably of the formula III-2a, more preferably these compounds of the formula III-2 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which

-   R³¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R³² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R³¹ and R³²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)), particularly preferably (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

The compounds of the formula III-3 are preferably compounds of the formula III-3a:

in which

-   R³¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R³² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R³¹ and R³²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)), particularly preferably (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

The compounds of the formula III-4 are preferably compounds of the formula III-4a:

in which

-   R³¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R³² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R³¹ and R³²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)), particularly preferably (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

The compounds of the formula III-5 are preferably selected from the group of the compounds of the formulae III-5a and III-5b, preferably of the formula III-5a, more preferably these compounds of the formula III-5 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which

-   R³¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R³² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R³¹ and R³²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)), particularly preferably (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

The compounds of the formula III-6 are preferably selected from the group of the compounds of the formulae III-6a and III-6b, more preferably these compounds of the formula III-6 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which

-   R³¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R³² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R³¹ and R³²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)), particularly preferably (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

The media in accordance with the present invention optionally comprise one or more compounds of the formula IV

in which

-   R⁴¹ and R⁴², independently of one another, denote H, unfluorinated     alkyl or alkoxy having 1 to 15, preferably 3 to 10, C atoms or     unfluorinated alkenyl, alkenyloxy or alkoxyalkyl having 2 to 15,     preferably 3 to 10, C atoms, preferably unfluorinated alkyl or     alkenyl,     one of -   Z⁴¹ and Z⁴² denotes trans-CH═CH—, trans-CF═CF— or —C≡C— and the     other denotes, independently thereof, trans-CH═CH—, trans-CF═CF— or     a single bond, preferably one of them denotes —C≡C— or trans-CH═CH—     and the other denotes a single bond, and

-   -   independently of one another, denote

The liquid-crystalline media in accordance with the present application preferably comprise in total 0 to 40%, preferably 0 to 30% and particularly preferably 5 to 25%, of compounds of the formula IV.

The compounds of the formulae IV are preferably selected from the group of the compounds of the formulae IV-1 to IV-3, more preferably these compounds of the formula IV predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which one of

-   Y⁴¹ and Y⁴² denotes H and the other denotes H or F, and -   R⁴¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R⁴² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R⁴¹ and R⁴²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)), particularly preferably (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

The compounds of the formulae IV-1 are preferably selected from the group of the compounds of the formulae IV-1a to IV-1c, more preferably these compounds of the formula IV-1 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which

-   R⁴¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R⁴² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R⁴¹ and R⁴²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)), particularly preferably (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

The compounds of the formula IV-2 are preferably compounds of the formula IV-2a:

in which

-   R⁴¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R⁴² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R⁴¹ and R⁴²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)), C_(n)H_(2n+1) and O—C_(m)H_(2m+1)) and (CH₂═CH—(CH₂)_(Z) and C_(m)H_(2m+1)), particularly preferably (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

The compounds of the formula IV-3 are preferably compounds of the formula IV-3a:

in which

-   R⁴¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R⁴² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R⁴¹ and R⁴²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)).

The media in accordance with the present invention optionally comprise one or more compounds of the formula V

in which

-   L⁵¹ denotes R⁵¹ or X⁵¹, -   L⁵² denotes R⁵² or X⁵², -   R⁵¹ and R⁵², independently of one another, denote H, unfluorinated     alkyl or alkoxy having 1 to 15, preferably 3 to 10, C atoms or     unfluorinated alkenyl, alkenyloxy or alkoxyalkyl having 2 to 15,     preferably 3 to 10, C atoms, preferably unfluorinated alkyl or     alkenyl, -   X⁵¹ and X⁵², independently of one another, denote H, F, Cl, —CN,     —NCS, —SF₅, fluorinated alkyl or fluorinated alkoxy having 1 to 7 C     atoms or fluorinated alkenyl, unfluorinated or fluorinated     alkenyloxy or unfluorinated or fluorinated alkoxyalkyl having 2 to 7     C atoms, preferably fluorinated alkoxy, fluorinated alkenyloxy, F or     Cl, and -   Z⁵¹ to Z⁵³, independently of one another, denote trans-CH═CH—,     trans-CF═CF—, —C≡C— or a single bond, preferably one or more of them     denotes a single bond, and particularly preferably all denote a     single bond,

-   -   independently of one another, denote

The compounds of the formula V are preferably selected from the group of the compounds of the formulae V-1 to V-3, more preferably these compounds of the formula V predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which the parameters have the respective meanings indicated above under formula V and preferably one of

and in which

-   R⁵¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R⁵² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R⁵¹ and R⁵²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)).

The liquid-crystalline media in accordance with the present application preferably comprise in total 5 to 30%, preferably 10 to 25% and particularly preferably 15 to 20%, of compounds of the formula V.

The compounds of the formula V-1 are preferably selected from the group of the compounds of the formulae V-1a to V-1e, more preferably these compounds of the formula V-1 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which the parameters have the meaning given above and preferably

-   R⁵¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1), and -   n denotes an integer in the range from 0 to 15, preferably in the     range from 1 to 7 and particularly preferably 1 to 5, and -   X⁵² preferably denotes F or Cl.

The compounds of the formula V-2 are preferably selected from the group of the compounds of the formulae V-2a and V-2b, more preferably these compounds of the formula V-2 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:

in which

-   R⁵¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R⁵² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combination of (R⁵¹ and R⁵²) here is, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)).

The compounds of the formula V-3 are preferably compounds of the formulae V-3a and V-3b:

in which

-   R⁵¹ has the meaning indicated above and preferably denotes     C_(n)H_(2n+1) or CH₂═CH—(CH₂)_(Z), and -   R⁵² has the meaning indicated above and preferably denotes     C_(m)H_(2m+1) or O—C_(m)H_(2m+1) or (CH₂)_(Z)—CH═CH₂, and in which -   n and m, independently of one another, denote an integer in the     range from 0 to 15, preferably in the range from 1 to 7 and     particularly preferably 1 to 5, and -   z denotes 0, 1, 2, 3 or 4, preferably 0 or 2.

The preferred combinations of (R⁵¹ and R⁵²) here are, in particular, (C_(n)H_(2n+1) and C_(m)H_(2m+1)) and (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)), particularly preferably (C_(n)H_(2n+1) and O—C_(m)H_(2m+1)).

In a preferred embodiment of the present invention, the medium comprises one or more dielectrically positive compounds of the formula I-1 having a dielectric anisotropy of greater than 3.

The medium preferably comprises one or more dielectrically neutral compounds of the formula I-2 having a dielectric anisotropy in the range from more than −1.5 to 3.

In a preferred embodiment of the present invention, the medium comprises one or more compounds of the formula II.

In a further preferred embodiment of the present invention, the medium comprises one or more compounds of the formula III.

The liquid-crystalline media in accordance with the present invention preferably comprise 10% or less, preferably 5% or less, particularly preferably 2% or less, very particularly preferably 1% or less, and in particular absolutely no compound having only two or fewer five- and/or six-membered rings.

The definitions of the abbreviations (acronyms) are likewise indicated below in Table D or are evident from Tables A to C.

The liquid-crystalline media in accordance with the present invention preferably comprise, more preferably predominantly consist of, even more preferably essentially consist of and very preferably completely consist of compounds selected from the group of the compounds of the formulae I to V, preferably I to IV and very preferably I to III and/or V.

In this application, comprise in connection with compositions means that the entity in question, i.e. the medium or the component, comprises the component or components or compound or compounds indicated, preferably in a total concentration of 10% or more and very preferably 20% or more.

In this connection, predominantly consist of means that the entity in question comprises 55% or more, preferably 60% or more and very preferably 70% or more of the component or components or compound or compounds indicated.

In this connection, essentially consist of means that the entity in question comprises 80% or more, preferably 90% or more and very preferably 95% or more of the component or components or compound or compounds indicated.

In this connection, completely consist of means that the entity in question comprises 98% or more, preferably 99% or more and very preferably 100.0% of the component or components or compound or compounds indicated.

Other mesogenic compounds which are not explicitly mentioned above can optionally and advantageously also be used in the media in accordance with the present invention. Such compounds are known to the person skilled in the art.

The liquid-crystal media in accordance with the present invention preferably have a clearing point of 90° C. or more, more preferably 100° C. or more, still more preferably 120° C. or more, particularly preferably 150° C. or more and very particularly preferably 170° C. or more.

The nematic phase of the media in accordance with the invention preferably extends at least from 20° C. or less to 90° C. or more, preferably up to 100° C. or more, more preferably at least from 0° C. or less to 120° C. or more, very preferably at least from −10° C. or less to 140° C. or more and in particular at least from −20° C. or less to 150° C. or more.

The Δ∈ of the liquid-crystal medium in accordance with the invention, at 1 kHz and 20° C., is preferably 1 or more, more preferably 2 or more and very preferably 3 or more.

The Δn of the liquid-crystal media in accordance with the present invention, at 589 nm (Na^(D)) and 20° C., is preferably in the range from 0.200 or more to 0.90 or less, more preferably in the range from 0.250 or more to 0.90 or less, even more preferably in the range from 0.300 or more to 0.85 or less and very particularly preferably in the range from 0.350 or more to 0.800 or less.

In a first preferred embodiment of the present application, the Δn of the liquid-crystal media in accordance with the present invention is preferably 0.50 or more, more preferably 0.55 or more.

In accordance with the present invention, the individual compounds of the formula I are preferably used in a total concentration of 10% to 70%, more preferably 20% to 60%, even more preferably 30% to 50% and very preferably 25% to 45% of the mixture as a whole.

The compounds of the formula II are preferably used in a total concentration of 1% to 20%, more preferably 1% to 15%, even more preferably 2% to 15% and very preferably 3% to 10% of the mixture as a whole.

The compounds of the formula III are preferably used in a total concentration of 1% to 60%, more preferably 5% to 50%, even more preferably 10% to 45% and very preferably 15% to 40% of the mixture as a whole.

The liquid-crystal media preferably comprise, preferably predominantly consist of and very preferably completely consist of in total 50% to 100%, more preferably 70% to 100% and very preferably 80% to 100% and in particular 90% to 100% of the compounds of the formulae I, II, III, IV and V, preferably of the formulae I, III, IV and V, more preferably of the formulae I, II, III, IV and/or VI.

In the present application, the expression dielectrically positive describes compounds or components where Δ∈>3.0, dielectrically neutral describes those where −1.5≦Δ∈≦3.0 and dielectrically negative describes those where Δ∈<−1.5. Δ∈ is determined at a frequency of 1 kHz and at 20° C. The dielectric anisotropy of the respective compound is determined from the results of a solution of 10% of the respective individual compound in a nematic host mixture. If the solubility of the respective compound in the host mixture is less than 10%, the concentration is reduced to 5%. The capacitances of the test mixtures are determined both in a cell having homeotropic alignment and in a cell having homogeneous alignment. The cell thickness of both types of cells is approximately 20 μm. The voltage applied is a rectangular wave having a frequency of 1 kHz and an effective value of typically 0.5 V to 1.0 V, but it is always selected to be below the capacitive threshold of the respective test mixture.

Δ∈ is defined as (∈∥−∈⊥), while ∈_(ave.) is (∈∥+2∈⊥)/3.

The host mixture used for dielectrically positive compounds is mixture ZLI-4792 and that used for dielectrically neutral and dielectrically negative compounds is mixture ZLI-3086, both from Merck KGaA, Germany. The absolute values of the dielectric constants of the compounds are determined from the change in the respective values of the host mixture on addition of the compounds of interest. The values are extrapolated to a concentration of the compounds of interest of 100%.

Components having a nematic phase at the measurement temperature of 20° C. are measured as such, all others are treated like compounds.

The expression threshold voltage in the present application refers to the optical threshold and is quoted for 10% relative contrast (V₁₀), and the expression saturation voltage refers to the optical saturation and is quoted for 90% relative contrast (V₉₀), in both cases unless expressly stated otherwise. The capacitive threshold voltage (V₀), also called the Freedericks threshold (V_(Fr)), is only used if expressly mentioned.

The parameter ranges indicated in this application all include the limit values, unless expressly stated otherwise.

The different upper and lower limit values indicated for various ranges of properties in combination with one another give rise to additional preferred ranges.

Throughout this application, the following conditions and definitions apply, unless expressly stated otherwise. All concentrations are quoted in percent by weight and relate to the respective mixture as a whole, all temperatures are quoted in degrees Celsius and all temperature differences are quoted in differential degrees. All physical properties are determined in accordance with “Merck Liquid Crystals, Physical Properties of Liquid Crystals”, Status November 1997, Merck KGaA, Germany, and are quoted for a temperature of 20° C., unless expressly stated otherwise. The optical anisotropy (Δn) is determined at a wavelength of 589.3 nm. The dielectric anisotropy (Δ∈) is determined at a frequency of 1 kHz. The threshold voltages, as well as all other electro-optical properties, are determined using test cells produced at Merck KGaA, Germany. The test cells for the determination of Δ∈ have a cell thickness of approximately 20 μm. The electrode is a circular ITO electrode having an area of 1.13 cm² and a guard ring. The orientation layers are SE-1211 from Nissan Chemicals, Japan, for homeotropic orientation (∈∥) and polyimide AL-1054 from Japan Synthetic Rubber, Japan, for homogeneous orientation (∈⊥). The capacitances are determined using a Solatron 1260 frequency response analyser using a sine wave with a voltage of 0.3 V_(rms). The light used in the electro-optical measurements is white light. A set-up using a commercially available DMS instrument from Autronic-Melchers, Germany, is used here. The characteristic voltages have been determined under perpendicular observation. The threshold (V₁₀), mid-grey (V₅₀) and saturation (V₉₀) voltages have been determined for 10%, 50% and 90% relative contrast, respectively.

The liquid-crystalline media are investigated with respect to their properties in the microwave frequency range as described in A. Penirschke, S. Müller, P. Scheele, C. Weil, M. Wittek, C. Hock and R. Jakoby: “Cavity Perturbation Method for Characterization of Liquid Crystals up to 35 GHz”, 34^(th) European Microwave Conference—Amsterdam, pp. 545-548.

Compare in this respect also A. Gaebler, F. Gölden, S. Müller, A. Penirschke and R. Jakoby “Direct Simulation of Material Permittivites . . . ”, 12MTC 2009—International Instrumentation and Measurement Technology Conference, Singapore, 2009 (IEEE), pp. 463-467, and DE 10 2004 029 429 A, in which a measurement method is likewise described in detail.

The liquid crystal is introduced into a polytetrafluoroethylene (PTFE) capillary. The capillary has an internal radius of 180 μm and an external radius of 350 μm. The effective length is 2.0 cm. The filled capillary is introduced into the centre of the cavity with a resonance frequency of 30 GHz. This cavity has a length of 6.6 mm, a width of 7.1 mm and a height of 3.6 mm. The input signal (source) is then applied, and the result of the output signal is recorded using a commercial vector network analyser.

The change in the resonance frequency and the Q factor between the measurement with the capillary filled with the liquid crystal and the measurement without the capillary filled with the liquid crystal is used to determine the dielectric constant and the loss angle at the corresponding target frequency by means of equations 10 and 11 in A. Penirschke, S. Müller, P. Scheele, C. Weil, M. Wittek, C. Hock and R. Jakoby: “Cavity Perturbation Method for Characterization of Liquid Crystals up to 35 GHz”, 34^(th) European Microwave Conference—Amsterdam, pp. 545-548, as described therein.

The values for the components of the properties perpendicular and parallel to the director of the liquid crystal are obtained by alignment of the liquid crystal in a magnetic field. To this end, the magnetic field of a permanent magnet is used. The strength of the magnetic field is 0.35 tesla. The alignment of the magnets is set correspondingly and then rotated correspondingly through 90°.

Preferred components are phase shifters, varactors, wireless and radio wave antenna arrays, matching circuit adaptive filters and others.

In the present application, the term compounds is taken to mean both one compound and a plurality of compounds, unless expressly stated otherwise.

The liquid-crystal media according to the invention preferably have nematic phases of in each case at least from −20° C. to 80° C., preferably from −30° C. to 85° C. and very particularly preferably from −40° C. to 100° C. The phase particularly preferably extends to 120° C. or more, preferably to 140° C. or more and very particularly preferably to 180° C. or more. The expression have a nematic phase here means on the one hand that no smectic phase and no crystallisation are observed at low temperatures at the corresponding temperature and on the other hand that no clearing occurs on heating from the nematic phase. The investigation at low temperatures is carried out in a flow viscometer at the corresponding temperature and checked by storage in test cells having a layer thickness of 5 μm for at least 100 hours. At high temperatures, the clearing point is measured in capillaries by conventional methods.

Furthermore, the liquid-crystal media according to the invention are characterised by high optical anisotropy values. The birefringence at 589 nm is preferably 0.20 or more, particularly preferably 0.25 or more, particularly preferably 0.30 or more, particularly preferably 0.40 or more and very particularly preferably 0.45 or more. In addition, the birefringence is preferably 0.80 or less.

The liquid crystals employed preferably have a positive dielectric anisotropy. This is preferably 2 or more, preferably 4 or more, particularly preferably 6 or more and very particularly preferably 10 or more.

Furthermore, the liquid-crystal media according to the invention are characterised by high anisotropy values in the microwave range. The birefringence at about 8.3 GHz is, for example, preferably 0.14 or more, particularly preferably 0.15 or more, particularly preferably 0.20 or more, particularly preferably 0.25 or more and very particularly preferably 0.30 or more. In addition, the birefringence is preferably 0.80 or less.

The material quality η(μ-waves)/tan(δ) of the preferred liquid-crystal materials is 5 or more, preferably 6 or more, preferably 8 or more, preferably 10 or more, preferably 15 or more, preferably 17 or more, particularly preferably 20 or more and very particularly preferably 25 or more.

The preferred liquid-crystal materials have phase shifter qualities of 15°/dB or more, preferably 20°/dB or more, preferably 30°/dB or more, preferably 40°/dB or more, preferably 50°/dB or more, particularly preferably 80°/dB or more and very particularly preferably 100°/dB or more.

In some embodiments, however, liquid crystals having a negative value of the dielectric anisotropy can also advantageously be used.

The liquid crystals employed are either individual substances or mixtures. They preferably have a nematic phase.

The term “alkyl” preferably encompasses straight-chain and branched alkyl groups having 1 to 15 carbon atoms, in particular the straight-chain groups methyl, ethyl, propyl, butyl, pentyl, hexyl and heptyl. Groups having 2 to 10 carbon atoms are generally preferred.

The term “alkenyl” preferably encompasses straight-chain and branched alkenyl groups having 2 to 15 carbon atoms, in particular the straight-chain groups. Particularly preferred alkenyl groups are C₂- to C₇-1 E-alkenyl, C₄- to C₇-3E-alkenyl, C₅- to C₇-4-alkenyl, C₆- to C₇-5-alkenyl and C₇-6-alkenyl, in particular C₂- to C₇-1 E-alkenyl, C₄- to C₇-3E-alkenyl and C₅- to C₇-4-alkenyl. Examples of further preferred alkenyl groups are vinyl, 1 E-propenyl, 1 E-butenyl, 1 E-pentenyl, 1 E-hexenyl, 1 E-heptenyl, 3-butenyl, 3E-pentenyl, 3E-hexenyl, 3E-heptenyl, 4-pentenyl, 4Z-hexenyl, 4E-hexenyl, 4Z-heptenyl, 5-hexenyl, 6-heptenyl and the like. Groups having up to 5 carbon atoms are generally preferred.

The term “fluoroalkyl” preferably encompasses straight-chain groups having a terminal fluorine, i.e. fluoromethyl, 2-fluoroethyl, 3-fluoropropyl, 4-fluorobutyl, 5-fluoropentyl, 6-fluorohexyl and 7-fluoroheptyl. However, other positions of the fluorine are not excluded.

The term “oxaalkyl” or “alkoxyalkyl” preferably encompasses straight-chain radicals of the formula C_(n)H_(2n+1)—O—(CH₂)_(m), in which n and m each, independently of one another, denote 1 to 10. Preferably, n is 1 and m is 1 to 6.

Compounds containing a vinyl end group and compounds containing a methyl end group have low rotational viscosity.

In the present application, both high-frequency technology and hyper-frequency technology denote applications having frequencies in the range from 1 MHz to 1 THz, preferably from 1 GHz to 500 GHz, more preferably 2 GHz to 300 GHz, particularly preferably from about 5 to 150 GHz.

The liquid-crystal media in accordance with the present invention may comprise further additives and chiral dopants in the usual concentrations. The total concentration of these further constituents is in the range from 0% to 10%, preferably 0.1% to 6%, based on the mixture as a whole. The concentrations of the individual compounds used are each preferably in the range from 0.1% to 3%. The concentration of these and similar additives is not taken into consideration when quoting the values and concentration ranges of the liquid-crystal components and liquid-crystal compounds of the liquid-crystal media in this application.

The liquid-crystal media according to the invention consist of a plurality of compounds, preferably 3 to 30, more preferably 4 to 20 and very preferably 4 to 16 compounds. These compounds are mixed in a conventional manner. In general, the desired amount of the compound used in the smaller amount is dissolved in the compound used in the larger amount. If the temperature is above the clearing point of the compound used in the higher concentration, it is particularly easy to observe completion of the dissolution process. It is, however, also possible to prepare the media in other conventional ways, for example using so-called pre-mixes, which can be, for example, homologous or eutectic mixtures of compounds, or using so-called “multibottle” systems, the constituents of which are themselves ready-to-use mixtures.

All temperatures, such as, for example, the melting point T(C,N) or T(C,S), the transition from the smectic (S) to the nematic (N) phase T(S,N) and the clearing point T(N,I) of the liquid crystals, are quoted in degrees Celsius. All temperature differences are quoted in differential degrees.

In the present invention and especially in the following examples, the structures of the mesogenic compounds are indicated by means of abbreviations, also referred to as acronyms. In these acronyms, the chemical formulae are abbreviated as follows using Tables A to C below. All groups C_(n)H_(2n+1), C_(m)H_(2m+1) and C_(l)H_(2l+1) or C_(n)H_(2n−1)) C_(m)H_(2m−1) and C_(l)H_(2l−1) denote straight-chain alkyl or alkenyl, preferably 1-E-alkenyl, respectively, in each case having n, m or l C atoms. Table A lists the codes used for the ring elements of the core structures of the compounds, while Table B shows the linking groups. Table C gives the meanings of the codes for the left-hand or right-hand end groups. Table D shows illustrative structures of compounds with their respective abbreviations.

TABLE A Ring elements

TABLE B Linking groups E —CH₂CH₂— Z —CO—O— V —CH═CH— ZI —O—CO— X —CF═CH— O —CH₂—O— XI —CH═CF— OI —O—CH₂— B —CF═CF— Q —CF₂—O— T —C≡C— QI —O—CF₂— W —CF₂CF₂—

TABLE C End groups Left-hand side Right-hand side Use alone -n- C_(n)H_(2n+1)— -n —C_(n)H_(2n+1) -nO- C_(n)H_(2n+1)—O— -nO —O—C_(n)H_(2n+1) -V- CH₂═CH— -V —CH═CH₂ -nV- C_(n)H_(2n+1)—CH═CH— -nV —C_(n)H_(2n)—CH═CH₂ -Vn- CH₂═CH—C_(n)H_(2n+1)— -Vn —CH═CH—C_(n)H_(2n+1) -nVm- C_(n)H_(2n+1)—CH═CH—C_(m)H_(2m)— -nVm —C_(n)H_(2n)—CH═CH—C_(m)H_(2m+1) -N- N≡C— -N —C≡N -S- S═C═N— -S —N═C═S -F- F— -F —F -CL- Cl— -CL —Cl -M- CFH₂— -M —CFH₂ -D- CF₂H— -D —CF₂H -T- CF₃— -T —CF₃ -MO- CFH₂O— -OM —OCFH₂ -DO- CF₂HO— -OD —OCF₂H -TO- CF₃O— -OT —OCF₃ -OXF- CF₂═CH—O— -OXF —O—CH≡CF₂ -A- H—C≡C— -A —C≡C—H -nA- C_(n)H_(2n+1)—C≡C— -An —C≡C—C_(n)H_(2n+1) -NA- N≡C—C≡C— -AN —C≡C—C≡N Use together with others -...A...- —C≡C— -...A... —C≡C— -...V...- CH═CH— -...V... —CH═CH— -...Z...- —CO—O— -...Z... —CO—O— -...ZI...- —O—CO— -...ZI... —O—CO— -...K...- —CO— -...K... —CO— -...W...- —CF═CF— -...W... —CF═CF— in which n and m each denote integers, and the three dots “...” are place-holders for other abbreviations from this table.

The following table shows illustrative structures together with their respective abbreviations. These are shown in order to illustrate the meaning of the rules for the abbreviations. They furthermore represent compounds which are preferably used.

TABLE D Illustrative structures The illustrative structures are compounds having three 6-membered rings which are particularly preferably employed:

The illustrative structures are compounds having four 6-membered rings which are particularly preferably employed:

Illustrative structures of dielectrically neutral compounds which are preferably employed:

Illustrative structures of further compounds which are preferably employed:

The following table, Table E, shows illustrative compounds which can be used as stabiliser in the mesogenic media in accordance with the present invention. The total concentration of these and similar compounds in the media is preferably 5% or less.

TABLE E

In a preferred embodiment of the present invention, the mesogenic media comprise one or more compounds selected from the group of the compounds from Table E.

The following table, Table F, shows illustrative compounds which can preferably be used as chiral dopants in the mesogenic media in accordance with the present invention.

TABLE F

In a preferred embodiment of the present invention, the mesogenic media comprise one or more compounds selected from the group of the compounds from Table F.

The mesogenic media in accordance with the present application preferably comprise two or more, preferably four or more, compounds selected from the group consisting of the compounds from the above tables.

The liquid-crystal media in accordance with the present invention preferably comprise

-   -   seven or more, preferably eight or more, compounds, preferably         compounds having three or more, preferably four or more,         different formulae, selected from the group of the compounds         from Table D.

EXAMPLES

The following examples illustrate the present invention without limiting it in any way.

However, it is clear to the person skilled in the art from the physical properties what properties can be achieved and in what ranges they can be modified. In particular, the combination of the various properties which can preferably be achieved is thus well defined for the person skilled in the art.

Example 1

A liquid-crystal mixture M-1 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-5-CL 26.0 2 PGIGI-3-CL 8.0 3 PGIGI-5-CL 20.0 4 PGIGI-5-F 9.0 5 PPTY-3-4 3.0 6 PYGP-3-5 5.0 7 PYGP-5-3 5.0 8 CGPC-3-5 3.0 9 CGPC-5-5 5.0 10  CPGP-5-2 8.0 11  CPGP-5-3 8.0 Σ 100.0 Physical properties T(N, I) = 171° C. n_(e) (20° C., 589.3 nm) = 1.7859 Δn (20° C., 589.3 nm) = 0.2954 ε_(||) (20° C., 1 kHz) = 6.4 Δε (20° C., 1 kHz) = 2.0 γ₁ (20° C.) = 650 mPa · s

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

TABLE 1 Properties of mixture M-1 at 30 GHz T/° C. ε_(r, ⊥) ε_(r, ||) tan δ_(ε r, ⊥) tan δ_(ε r, ||) τ_(ε r) η 11.27 2.40 2.97 0.0109 0.0026 0.19 17.45 29.71 2.41 2.97 0.0159 0.0037 0.19 11.70 58.28 2.41 2.97 0.0252 0.0061 0.18 7.07 87.50 2.40 2.89 0.0372 0.0097 0.17 4.51 Note: at 20° C., the following is obtained approximately by intrapolation: Δε_(r⊥) = 0.56, tan δ_(ε r, ⊥) = 0.013 and η = 14.5.

For comparison, the compound 4′-pentyl-4-cyanobiphenyl (also called 5CB or K15, Merck KGaA) gives tan δ_(∈ r,⊥)=0.026 and η=4.3 at 20° C.

TABLE 2 Comparison of the properties at 30 GHz and 20° C. Example Liquid crystal Δε_(r⊥) δ_(ε r,⊥) η 1 M-1 0.56 0.013 14.5 2 M-2 0.56 0.014 15 Comparison 5CB 0.026 4.3

Example 2

A liquid-crystal mixture M-2 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-5-CL 26.0 2 PGIGI-3-CL 8.0 3 PGIGI-5-CL 20.0 4 PGIGI-5-F 5.0 5 PPTY-3-4 3.0 6 PYGP-4-4 4.0 7 PYGP-5-3 5.0 8 CCZPC-3-5 3.0 9 CGPC-3-5 3.0 10  CGPC-5-5 5.0 11  CPGP-5-2 8.0 12  CPGP-5-3 8.0 Σ 100.0 Physical properties T(N, I) = 179.5° C. n_(e) (20° C., 589.3 nm) = 1.7861 Δn (20° C., 589.3 nm) = 0.3118

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

TABLE 3 Properties of mixture M-2 at 30 GHz T/° C. ε_(r, ⊥) ε_(r, ||) tan δ_(ε r, ⊥) tan δ_(ε r, ||) τ_(ε r) FoM 11.49 2.41 2.98 0.0108 0.0028 0.19 17.77 20.29 2.42 2.98 0.0130 0.0033 0.19 14.50 25.02 2.42 2.97 0.0143 0.0035 0.19 13.08 29.80 2.42 2.97 0.0155 0.0038 0.19 11.99 34.55 2.42 2.96 0.0169 0.0041 0.18 10.95 58.29 2.41 2.93 0.0246 0.0062 0.18 7.20 77.56 2.40 2.90 0.0319 0.0087 0.17 5.36 97.57 2.40 2.86 0.0406 0.0116 0.16 4.00 Note: at 20° C., the following is obtained approximately by intrapolation: Δε_(r⊥) = 0.56, tan δ_(ε r, ⊥) = 0.014 and η = 15.

Example 3

A liquid-crystal mixture M-3 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-3-CL 10.0 2 GGP-5-CL 20.0 3 PPTUI-3-2 20.0 4 PPTUI-3-4 20.0 5 PPTUI-4-4 16.0 6 CPGP-5-2 7.0 7 CPGP-5-3 7.0 Σ 100.0 Physical properties T(N, I) = 170.1° C. n_(e) (20° C., 589.3 nm) = 1.5267 Δn (20° C., 589.3 nm) = 0.2918 ε_(||) (20° C., 1 kHz) = 7.8 Δε (20° C., 1 kHz) = 4.4 γ₁ (20° C.) = 698 mPa · s

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 4

A liquid-crystal mixture M-4 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-3-CL 10.0 2 GGP-5-CL 19.0 3 PPTUI-3-2 18.0 4 PPTUI-3-4 18.0 5 PPTUI-4-4 10.0 6 PGIGP-3-5 6.00 7 PPGU-3-F 3.00 8 CPGP-5-2 8.0 9 CPGP-5-3 8.0 Σ 100.0 Physical properties T(N, I) = 183.5° C. Δn (20° C., 589.3 nm) = 0.283 ε_(||) (20° C., 1 kHz) = 8.0 Δε (20° C., 1 kHz) = 3.5 γ₁ (20° C.) = 753 mPa · s

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 5

A liquid-crystal mixture M-5 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-3-CL 10.0 2 GGP-5-CL 17.0 3 PPTUI-3-2 13.0 4 PPTUI-3-4 13.0 5 PPTUI-4-4 10.0 6 PPGU-3-F 3.0 7 PPGU-4-F 3.0 8 PPGU-V2-F 3.0 9 PGIGP-3-5 7.0 10  PGIGP-5-5 7.0 11  CPGP-5-2 7.0 12  CPGP-5-3 7.0 Σ 100.0 Physical properties

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 6

A liquid-crystal mixture M-6 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-5-CL 17.0 2 PPTUI-3-2 20.0 3 PPTUI-3-4 20.0 4 PPTUI-4-4 10.0 5 PPGU-3-F 3.0 6 PPGU-4-F 3.0 7 PPGU-V2-F 3.0 8 PGIGP-3-4 5.0 9 PGIGP-3-5 5.0 10  CPGP-5-2 7.0 11  CPGP-5-3 7.0 Σ 100.0 Physical properties T(N, I) = 198.0° C. ε_(||) (20° C., 1 kHz) = 7.7 Δε (20° C., 1 kHz) = 3.5

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 7

A liquid-crystal mixture M-7 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-3-CL 10.0 2 GGP-5-CL 20.0 3 PPTUI-3-2 15.0 4 PPTUI-3-4 20.0 5 PPGU-3-F 3.0 6 PPGU-4-F 3.0 7 PPGU-V2-F 3.0 8 PGIGP-3-4 5.0 9 PGIGP-3-5 5.0 10  CPGP-5-2 8.0 11  CPGP-5-3 8.0 Σ 100.0 Physical properties T(N, I) = 193.0° C. ε_(||) (20° C., 1 kHz) = 8.7 Δε (20° C., 1 kHz) = 3.5

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 8

A liquid-crystal mixture M-8 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-3-CL 10.0 2 GGP-5-CL 19.0 3 PPTUI-3-2 18.0 4 PPTUI-3-4 18.0 5 PPTUI-4-4 10.0 6 PPGU-3-F 2.0 7 PPGU-4-F 2.0 8 PPGU-V2-F 2.0 9 PGIGP-3-5 5.0 10  CPGP-5-2 7.0 11  CPGP-5-3 7.0 Σ 100.0 Physical properties

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 9

A liquid-crystal mixture M-9 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 PGP-2-5 10.0 2 PGP-3-4 10.0 3 PGP-3-7 15.0 4 PGP-2-2V 5.0 5 PYP-2-2V 10.0 6 PYP-2-4 10.0 7 PYP-2-5 20.0 8 PYP-3-5 15.0 9 PGIGP-3-5 5.0 Σ 100.0 Physical properties

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 10

A liquid-crystal mixture M-10 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-3-F 10.0 2 GGP-5-F 10.0 3 GGP-3-CL 10.0 4 GGP-4-CL 20.0 5 GGP-5-CL 20.0 6 GGP-6-CL 10.0 7 GGPP-5-3 5.0 8 PGGP-3-5 5.0 9 PGGP-3-6 5.0 10  PGGP-5-3 5.0 Σ 100.0 Physical properties T(N, I) = 134.5° C. n_(e) (20° C., 589.3 nm) = 1.8036 Δn (20° C., 589.3 nm) = 0.2774 ε_(||) (20° C., 1 kHz) = 15.2 Δε (20° C., 1 kHz) = 10.2 γ₁ (20° C.) = 758 mPa · s

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 11

A liquid-crystal mixture M-11 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-3-F 5.0 2 GGP-3-CL 10.0 3 GGP-4-CL 10.0 4 GGP-5-CL 15.0 5 GGP-5-3 20.0 6 PGP-2-5 10.0 7 PGP-3-7 15.0 8 PGP-2-2V 10.0 9 PGGP-3-5 5.0 Σ 100.0 Physical properties n_(e) (20° C., 589.3 nm) = 1.7885 Δn (20° C., 589.3 nm) = 0.2640 ε_(||) (20° C., 1 kHz) = 8.8 Δε (20° C., 1 kHz) = 4.7 γ₁ (20° C.) = 660 mPa · s

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 12

A liquid-crystal mixture M-12 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-3-CL 10.0 2 GGP-4-CL 20.0 3 GGP-5-CL 20.0 4 GGP-6-CL 10.0 5 GGP-5-3 25.0 6 PGGP-3-5 5.0 7 PGGP-3-6 5.0 8 PGGP-5-3 5.0 Σ 100.0 Physical properties T(N, I) = 124.5° C. n_(e) (20° C., 589.3 nm) = 1.7951 Δn (20° C., 589.3 nm) = 0.2709 ε_(||) (20° C., 1 kHz) = 11.6 Δε (20° C., 1 kHz) = 6.8 γ₁ (20° C.) = 895 mPa · s

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 13

A liquid-crystal mixture M-13 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-3-CL 5.0 2 GGP-5-CL 19.0 3 PGU-7-F 2.0 4 PPTUI-3-2 18.0 5 PPTUI-3-4 18.0 6 PPTUI-4-4 10.0 7 PPGU-7-F 2.0 8 PGIGP-3-5 6.0 9 DPGU-3-F 2.0 10  DPGU-3-OT 2.0 11  CPGP-5-2 8.0 12  CPGP-5-3 8.0 Σ 100.0 Physical properties T(N, I) = 184.5° C.

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

TABLE 4 Properties of mixture M-13 at 30 GHz T/° C. ε_(r, ⊥) ε_(r, ||) tan δ_(ε r, ⊥) tan δ_(ε r, ||) τ_(ε r) η 9.47 2.51 2.92 0.0094 0.0035 0.140 15.0 19.67 2.51 2.92 0.0115 0.0041 0.139 12.1 30.07 2.49 2.94 0.0135 0.0046 0.152 11.2 40.52 2.44 2.96 0.0169 0.0046 0.175 10.3 50.17 2.36 2.96 0.0214 0.0050 0.204 9.48 59.99 2.34 2.94 0.0246 0.0056 0.204 8.24 70.41 2.34 2.93 0.0276 0.0061 0.199 7.22 79.74 2.35 2.91 0.0291 0.0067 0.195 6.69 84.52 2.35 2.91 0.0295 0.0071 0.192 6.51 Note: at 20° C., the following is obtained approximately by intrapolation: Δε_(r⊥) = 2.51, tan δ_(ε r, ⊥) = 0.0115, τ_(ε r) = 0.140 and η = 14.5.

Example 14

A liquid-crystal mixture M-14 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-5-CL 20.0 2 PGU-3-CL 2.0 3 PGU-4-OT 2.0 4 PGP-F-OT 3.0 5 PPTUI-3-2 13.0 6 PPTUI-3-4 15.0 7 PPTUI-4-4 20.0 8 PPGU-7-F 2.0 9 PGIGP-3-5 6.0 10  CPTP-3-2 3.0 11  DPGU-3-F 2.0 12  DPGU-3-OT 2.0 13  CPGP-5-2 4.0 14  CPGP-5-3 6.0 Σ 100.0 Physical properties T(N, I) = 175.5° C.

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 15

A liquid-crystal mixture M-15 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-5-CL 10.0 2 GGP-6-CL 5.0 3 PGP-3-2V 3.0 4 PGP-2-2V 3.0 5 PPTUI-3-2 15.0 6 PPTUI-3-4 18.0 7 PPTUI-4-4 21.0 8 PPGU-7-F 2.0 9 PPGU-V2-F 2.0 10  PGIGP-3-5 7.0 11  CPTP-3-2 4.0 12  CPGU-3-OT 2.0 13  CPGU-4-OT 2.0 14  DPGU-3-OT 2.0 15  CPGP-5-2 4.0 Σ 100.0 Physical properties T(N, I) = 178° C.

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 16

A liquid-crystal mixture M-16 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-5-CL 20.0 2 GGP-5-3 12.0 3 PPTUI-3-2 12.0 4 PPTUI-3-4 16.0 5 PPTUI-4-4 20.0 6 PGUQU-5-F 5.0 7 PGGP-3-5 5.0 8 PGGP-3-6 4.0 9 APGP-3-3 3.0 10  APGP-3-4 3.0 Σ 100.0 Physical properties T(N, I) = 159.5° C. ε_(||) (20° C., 1 kHz) = 7.9 Δε (20° C., 1 kHz) = 4.3 γ₁ (20° C.) = 686 mPa · s

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters.

Example 17

A liquid-crystal mixture M-17 having the composition and properties as indicated in the following table is prepared.

Composition Compound No. Abbreviation 1 GGP-5-3 10.0 2 PPTUI-3-F 8.0 3 PPTUI-4-F 8.0 4 PPTUI-3-2 12.0 5 PPTUI-3-4 16.0 6 PPTUI-4-4 20.0 7 PPTUI-3-A4 5.0 8 PGUQU-5-F 7.0 9 PGGP-3-5 4.0 10  PGGP-3-6 4.0 11  APGP-3-3 3.0 12  APGP-3-4 3.0 Σ 100.0 Physical properties T(N, I) = 169° C.

This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters. 

1. Liquid-crystal medium, characterised in that it comprises at least one compound of the formula I and at least one compound of the formula II or at least one compound of the formula I and at least one compound of the formula III or at least one compound of the formula II and at least one compound of the formula III or at least one compound of the formula I and at least one compound of the formula II and at least one compound of the formula III:

in which L¹¹ denotes R¹¹ or X¹¹, L¹² denotes R¹² or X¹², R¹¹ and R¹², independently of one another, denote H, unfluorinated alkyl or unfluorinated alkoxy having 1 to 15 C atoms or unfluorinated alkenyl, unfluorinated alkenyloxy or unfluorinated alkoxyalkyl having 2 to 15 C atoms, X¹¹ and X¹², independently of one another, denote H, F, Cl, —CN, —NCS, —SF₅, fluorinated alkyl or fluorinated alkoxy having 1 to 7 C atoms or fluorinated alkenyl, unfluorinated alkenyloxy or unfluorinated or fluorinated alkoxyalkyl having 2 to 7 C atoms, and

independently of one another, denote

in which L²¹ denotes R²¹ and, in the case where Z²¹ and/or Z²² denote trans-CH═CH— or trans-CF═CF—, alternatively denotes X²¹, L²² denotes R²² and, in the case where Z²¹ and/or Z²² denote trans-CH═CH— or trans-CF═CF—, alternatively denotes X²², R²¹ and R²², independently of one another, denote H, unfluorinated alkyl or unfluorinated alkoxy having 1 to 17, preferably having 3 to 10, C atoms or unfluorinated alkenyl, unfluorinated alkenyloxy or unfluorinated alkoxyalkyl having 2 to 15, preferably 3 to 10, C atoms, X²¹ and X²², independently of one another, denote F or Cl, —CN, —NCS, —SF₅, fluorinated alkyl or fluorinated alkoxy having 1 to 7 C atoms or fluorinated alkenyl, fluorinated alkenyloxy or fluorinated alkoxyalkyl having 2 to 7 C atoms, one of Z²¹ and Z²² denotes trans-CH═CH—, trans-CF═CF— or —C≡C— and the other, independently thereof, denotes trans-CH═CH—, trans-CF═CF— or a single bond, and

independently of one another, denote

in which L³¹ denotes R³¹ or X³¹, L³² denotes R³² or X³², R³¹ and R³², independently of one another, denote H, unfluorinated alkyl or unfluorinated alkoxy having 1 to 17 C atoms or unfluorinated alkenyl, unfluorinated alkenyloxy or unfluorinated alkoxyalkyl having 2 to 15 C atoms, X³¹ and X³², independently of one another, denote H, F, Cl, —CN, —NCS, —SF₅, fluorinated alkyl or fluorinated alkoxy having 1 to 7 C atoms or fluorinated alkenyl, unfluorinated or fluorinated alkenyloxy or unfluorinated or fluorinated alkoxyalkyl having 2 to 7 C atoms, Z³¹ to Z³³, independently of one another, denote trans-CH═CH—, trans-CF═CF—, —C≡C— or a single bond, and

independently of one another, denote

and optionally one or more further compounds.
 2. Liquid-crystal medium according to claim 1, characterised in that it comprises one or more compounds of the formula I.
 3. Liquid-crystal medium according to claim 1, characterised in that it comprises one or more compounds of the formula II.
 4. Liquid-crystal medium according to claim 1, characterised in that it comprises one or more compounds of the formula III.
 5. Liquid-crystal medium according to claim 2, characterised in that the concentration of the compounds of the formula I in the medium is in the range from in total 15% to 70%.
 6. Liquid-crystal medium according to claim 3, characterised in that the concentration of the compounds of the formula II in the medium is in the range from in total 1% to 60%.
 7. Liquid-crystal medium according to claim 2, characterised in that it comprises one or more compounds selected from the group of the compounds of the formulae I-1 to I-3:

in which the parameters have the respective meanings given for formula I.
 8. Component for high-frequency technology, characterised in that it comprises a liquid crystal medium according to claim
 1. 9. Component according to claim 8, characterised in that it is suitable for operation in the microwave range.
 10. Component according to claim 8, characterised in that it is a phase shifter.
 11. (canceled)
 12. Process for the preparation of a liquid-crystal medium according to claim 1, characterised in that one or more compounds of the formula I are mixed with one or more compounds selected from the group of the compounds of the formulae II and/or III and optionally with one or more further compounds and/or with one or more additives.
 13. Microwave antenna array, characterised in that it comprises one or more components according to claim
 8. 